MASTER HYDRO

MASTER HYDROPropiedad Descripcin Valor Composicin Composition Superficie Surface: 72% Vinyl 28% PU Soporte Backing: 100% Microfiber polyester Peso Weight 853 g m Ancho Width 140 cm 2 % Grosor Thickness 1,2 mm Solidez a la luz Fastness to light 4 Resistencia a la traccin Tensile Strength ISO 1421 >333 N >180 N Resistencia al desgarro Tear Growth Resistance ISO 4674 1 Trama Weft: >28 N cm Urdimbre Warp: >25 N cm Flexiones Bally Flex Bally UNE 53243: 20 >100. 000

300 horas - hours Solidez a la luz / Fastness to light ISO 105 B02 → 7 Resistencia a la tracción / Tensile Strength ISO 13934-1 N/5 cm ≥ 170 Resistencia al desgarro / Tear Growth Resistance ISO 13937-2

Water column UNE-EN 20811 — >200 cm Tratamiento antibacteriano - antihongos / Antibacterial Treatment - Mildew Resistance Yes Tratamiento ignífugo / Fire Retardant UNE-EN 1021 Parts 1-2 BS 5852 Part 1 (Cigarette & Match) CAL TB 117-2013 Section E IMO Res

000 ciclos - cycles Anti hidrólisis / Anti hydrolysis Jungle Test No hydrolysis Tratamiento ignífugo / Fire Retardant Treatment UNE-EN 1021 Parts 1-2 BS 5852 Part 1 (Cigarette & Match)

Shrinkage               UNE-EN 26330:94 Trama - Weft: 0-22 %

Resistencia al agrietamiento en frío / Cold Crack Resistance ISO 17233:2017  -- Impermeabilidad

000 ciclos-cycles Antihidrólisis Jungle Test / Anti hydrolysis Jungle Test 8 semanas-weeks (10 años / years) Tratamiento ignífugo / Fire Retardant Treatment UNE-EN 1021 Parts 1/2

Solidez a la costura / Seam Strength EN ISO 13935-2:1999

Urdimbre - Warp: 650 N/5cm

3 mm Resistencia a la abrasión / Abrasion Test >100

Trama - Weft: 1294

9 N Urdimbre - Warp: 163

Urdimbre - Warp: >25 N Solidez a la costura / Seam Strength UNE-EN ISO 13935-2:2014